904L Stainless Steel Plate
تفاصيل المنتج
Product introduction
904L stainless steel is a non-stabilized austenitic stainless steel with low carbon content. This high alloy stainless steel is added with copper to improve its resistance to strong reducing acids, such as sulphuric acid. The steel is also resistant to stress corrosion cracking and crevice corrosion. 904L is non-magnetic, and offers excellent formability, toughness and weldability.
904L contains high amounts of expensive ingredients, such as molybdenum and nickel. Today, most of the applications that employ grade 904L are replaced by low-cost duplex stainless steel 2205.
| ITEM | Stainless Steel Sheet From China Facotry |
| Brand | BAOSTEEL, JISCO, TISCO, etc. |
| Grade |
201.202.301.302.304.304L.310S.316.316L.321.430.430A.309S.2205.2507.2520.430.630.631 .410.440.904Lect. Or Customized |
| Certificate |
SGS,BV,IQI,TUV,ISO,etc |
| Surface | No.1, 2B, BA, 8K Mirror, Hairline,satin, Embossed,brush,No.4,HL,matt,pvc film,laser film. |
| Standard | GB, AISI, ASTM, ASME, EN, BS, DIN, JIS |
| Package | Standard export sea-worthy packing or customized |
| MOQ | 1Ton |
Technical data
Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Cu | |
| 904L | min. max. |
- 0.02 |
- 2 |
- 1 |
- 0.045 |
- 0.035 |
19 23 |
4 5 |
23 28 |
1 2 |
Mechanical Properties
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) | Brinell (HB) | ||||
| 904L | 490 | 220 | 36 | 70-90 typical | 150 |
Physical Properties
| Grade | Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Elec Resistivity (nΩ.m) |
|||
| 0-100°C | 0-315°C | 0-538°C | At 20°C | At 500°C | |||||
| 904L | 7900 | 190 | 15 | - | - | 11.5 | - | 500 | 952 |
Grade Specification Comparison
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| 904L | N08904 | 904S13 | - | 1.4539 | X1NiCrMoCuN25-20-5 | 2562 | - |
Possible Alternative Grades
| Grade | Reasons for choosing grade 904L |
| 316L | A lower cost alternative, but with much lower corrosion resistance. |
| 6Mo | A higher resistance to pitting and crevice corrosion is needed. |
| 2205 | A very similar corrosion resistance, with the 2205 having higher mechanical strength, and at a lower cost to 904L. (2205 not suitable for temperatures above 300°C.) |
| Super duplex | Higher corrosion resistance is needed, together with a higher strength than 904L. |
Stainless Steel Seamless Pipe
Item |
Standard | ASTM A213/A213M | ASTM A312/A312M | JIS G 3459 | |||||||
| Grade | TP304 TP316 TP317 TP347 TP309H* |
TP304L TP316L TP317L TP310S TP310H* TP321H△ |
TP304 TP316 TP317 TP317 TP317* |
TP304L TP316L TP317L TP310S TP310H* TP321H△ |
SUS 304TB SUS 316TB SUS 317TB SUS 310TB SUS 321TB SUS 321HTB* |
SUS 304LTB SUS 316LTB SUS 317LTB SUS 310LTB SUS 347TB |
|||||
| Yield Strength | ≥170; ≥205 | ≥170; ≥205 | ≥170; ≥205 | ||||||||
| Tensile Strength | ≥485; ≥515 | ≥485; ≥515 | ≥485; ≥520 | ||||||||
| Elongation | ≥35 | ≥35 | ≥30; ≥35 | ||||||||
| Flattening test(mm) | H=1.09t/(0.09+t/D)and test completeness | H=1.09t/(0.09+t/D)and test completeness | H=1.09t/(0.09+t/D) | ||||||||
| Expanding test(mm) | Expanding rate of inside diameter is21-68％ | α=60° Expanding12%D | |||||||||
| Grain size | "*""△"ASTM E112"△"No.7or thicker | "*""△"ASTM E112"△"No.7or thicker | “*”、JIS G0551 7# or 7#above | ||||||||
| Hydraulic test(MPa) | D | Pmax | Hydraulic test p=220.6t/D designated by user and can be replaced by nondestructive flaw detection |
D | Pmax | ASTM A530 /A530M D≤270mm P=2Rt/D in the formula R=50%σ0.2 |
P=2Rt/D in the formula R=0.6σ s can be replaced by nonderstructive flaw detection |
||||
| <25.4 | 7 | ||||||||||
| 25.4-<38.1 | 10 | ≤88.9 | 17 | ||||||||
| 38.1-<50.8 | 14 | ||||||||||
| 50.8-<76.2 | 17 | >88.9 | 19 | ||||||||
| 76.2-<127 | 24 | ||||||||||
| ≥127 | 31 | ||||||||||
| Ntergranular corrosion test | ASTM A262 E method (supplemental requirement) | ASTM A262 E method (supplemental requirement) | JIS G0575(special requirement) | ||||||||
| Nondestructive flaw detection |
ASTM E213 E309 E426 | ASTM E213 E309 E426 | Can use eddy current or ultrasonic flaw detection eddy current JIS G0583EV ultrasonic JIS G0582 UD | ||||||||
| Heat treatment | Requirements | Requirements | Requirements | ||||||||
| Permitted variations in outside diameter (mm) |
Outside diameter | Permitted variations in outside diameter |
Outside diameter | Permitted variations | Outside diameter | Permitted variations | |||||
| <25.4 | ±0.10 | 10.3-48.3 | +0.40/-0.80 | <30 | ±0.3 | ||||||
| 25.4-≤38.1 | ±0.15 | >48.3-114.3 | +0.80/-0.80 | ||||||||
| >38.1-<50.8 | ±0.20 | >114.3-219.1 | +1.60/-0.80 | ||||||||
| 50.8-<63.5 | ±0.25 | >219.1-457.2 | +2.40/-0.80 | ≥30 | ±1% | ||||||
| 63.5-<76.2 | ±0.30 | >457.2-660.4 | +3.20/-0.80 | ||||||||
| 76.2-≤101.6 | ±0.38 | >660.4-864 | +4.00/-0.80 | ||||||||
| >101.6-≤190.5 | +0.38/-0.64 | >864-1219.2 | +4.80/-0.80 | ||||||||
| Permitted variations in wall thickness |
>190.5-≤228.6 | +0.38/-1.14 | Permitted variations in wall thickness（mm） ±12.5%t |
t<2 | ±0.2 | ||||||
| Outside diameter | Permitted variations in wall thickness |
||||||||||
| ≤38.1 | +20%t/-0 | t≥2 | ±10% | ||||||||
| >38.1 | +22%t/-0 | ||||||||||
| Bending | Reasonable straightness | Reasonable straightness | Practical straightness | ||||||||
| Other requirements | HRB<90 | HRB<90 | Hardness HRB<90(special requirement) | ||||||||
مصنع
شركة لياوتشنغ شينجو للصلب الخاص المحدودة، هي شركة شاملة تعمل في مجال الصلب عالي الجودة، والموقع الجغرافي ممتاز، والنقل مريح للغاية. تمتلك الشركة نظام جودة كامل وعلمي، وقد تم الاعتراف بالنزاهة والقوة وجودة المنتج من قبل الصناعة. تلتزم الشركة دائمًا بغرض الجودة العالية والتكلفة المنخفضة والوتيرة السريعة والخدمة الممتازة.لديه أكثر من 15 عامًا من الخبرة في التصدير تخدم مجموعة واسعة من العملاء من مختلف القطاعات. مثل الولايات المتحدة وأوروبا والشرق الأوسط وجنوب شرق آسيا وأفريقيا وأمريكا الجنوبية وغيرها من الأسواق. تتجاوز الصادرات السنوية 400000 طن.
التعبئة والتغليف والتسليم
التعبئة: ورق مقاوم للماء، وشريط فولاذي معبأ وغيرها من حزمة التصدير القياسية الصالحة للإبحار، أو حزمة مخصصة.
وقت التسليم: 7-15 أيام بعد الحصول على الوديعة.
طلب
نظرًا للمزايا العديدة الرائعة التي يتمتع بها الفولاذ المقاوم للصدأ، فإنه يستخدم على نطاق واسع في العديد من الصناعات. ويشمل ذلك الإنشاءات والأجهزة المنزلية والسيارات وإكسسوارات المطبخ والهياكل الميكانيكية وهندسة الديكور والصناعة الكيميائية وما إلى ذلك. دعونا نلقي نظرة موجزة.
شهادة
تتمتع شركة Liaocheng Xinju Special Steel المحدودة بنظام صارم لمراقبة الجودة يراقب عن كثب كل خطوة من خطوات التخزين والتفتيش والتعبئة والتغليف. لا يُسمح بأي أخطاء ولا يُسمح بتخزين المنتجات غير المؤهلة. تحظى شركة Shandong Chengshun Metal Materials المحدودة بثقة كبيرة ويدعمها العملاء بجودة المنتج الممتازة والخدمة الممتازة.
أسئلة وأجوبة
س : كيف يمكنني الحصول على الاقتباس الخاص بك في أقرب وقت ممكن ؟
ج : البريد الإلكتروني والفاكس سيتم فحصها في غضون 12 ساعة ، في حين أن سكايب ، مايكرو رسالة واتساب سوف تكون متاحة على الانترنت في غضون 24 ساعة . يرجى إرسال طلبك ومعلومات النظام ( الصلب الصف ، الحجم ، الكمية ، ميناء المقصد ) لنا ، ونحن سوف تجعل أفضل الأسعار في وقت قريب .
س : كيف نثق بك ؟
ج : نحن متخصصون في أعمال الصلب لسنوات عديدة ، ويقع المقر الرئيسي في مدينة ياوتشنغ بمقاطعة شاندونغ . مرحبا بكم في التحقيق بأي شكل من الأشكال ، من خلال أي وسيلة ، يمكنك وضع النظام في علي بابا ، وتقديم ضمان التجارة لضمان الدفع الخاص بك .
س : كيف يمكنك ضمان المنتج الخاص بك ؟
أ : كل منتج يتم تصنيعها من قبل ورشة عمل معتمدة ، ويتم تفتيشها وفقا لمعيار وطني لمراقبة الجودة / الجودة . نحن يستطيع أيضا زوّدت كفالة إلى زبونات أن يضمن النوعية .
س : هل تقبل طرف ثالث التفتيش ؟
ج : نعم ، نحن نقبل ذلك .
س : هل تقدم عينات ؟ هو حر أو إضافي ؟
ج : يمكن تقديم عينات للعملاء مجانا ، ولكن سيتم دفع رسوم الشحن عن طريق حساب العميل .
س : هل تسليم البضائع في الوقت المحدد ؟
ج : نعم ، نحن نعد لتقديم أفضل المنتجات ذات الجودة والتسليم في الوقت المحدد . الصدق هو هدف الشركة
منتجات ذات صلة
الحصول على اقتباس مجانا
اتصل بنا
تلفون . : +8619153115539
صندوق البريد : info@xjtmetal.com
WhatsApp : +8619153115539
عنوان：الغرفة 317، المنطقة ب، مستودع تشونججانجليان الداخلي، طريق ووييشان، منطقة التنمية الاقتصادية والتكنولوجية لياوتشنغ، مقاطعة شاندونغ
الحصول على اقتباس مجانا